U Shape Mosi2 Heating Elements at Good Price

• Customization: Available
• Name: Mosi2 Heater
• Max Temperature: 1700c
• Model NO.: 1700
• Transport Package: Wooden Boxes
• Specification: SGS
• Trademark: SHIBO
• Origin: Zhengzhou
• Production Capacity: 10000PCS/Month

Product Description

1.Molybdenum disilicide(MoSi2) heating element is a resistance generate-heating component made from MoSi2 or the basic material. It is used in high temperature under the oxidizing atmosphere, it looks like glass in its surface and form a light SiO2 glass film which can protect the element not to be oxidized. So this kind of element has unique effect for resisting oxidization in the high temperature. It is used to the highest temperature up to 1800°C during oxidizing atmosphere. And the applicable temperature is 500-1700°C.
2.Resistance property
The resistivity of element rapidly rises as the temperature rises. Under normal operating conditions, generally the element resistance doesn't change with the service time changing. So the old and new elements can be mixed used.
 
3.Phiscal property
 

Volume Density	5.5g/cm3	Porosity	7.40%
Bending Strength	15-25kg/cm3	Water absorption	1.20%
Vickers Hardness	(HV)570kg/mm2	Heating Elongation Rate	4%

 
4.Chemistry property
 
MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. When the temperature of element is more than 1700°C,the MoSi2 heating element must not be used in the temperature between 400°C and 700°C for a long time; otherwise the element will be cremated under the strong oxidizing function in the low temperature.

Details	Type:		1700C, 1800C
	Shape		U, W, ROD, UJL, WJL, and other special shape
	Diameters		3/6, 4/9, 6/12, 9/18, 12/24mm
	Lengths		Up to 2000mm
	Used temperature		1300C to 1800C
	Max. Using temperature		In oxidizing atmosphere, it can reach 1800C
Operation temperature  in different atmosphere		Atmosphere		1700type	1800type
		No2, O2, CO2, Air		1700	1800
		He, Ar, N		1650	1750
		SO2		1600	1700
		Co,N2		1150	1150
		Wet H2		1500	1600
		Dry H2		1350	1450
Application	MoSi2 heating element is used in the furnace temperature from 1300C to 1700C. It is extensively used in the industries of metallurgy, magnetic materials, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture, lab  furnace, Laboratory furnace, industry furnace, glass furnace, ceramic furnace etc.